PENGARUH POST CURING TIME TERHADAP PERBEDAAN KEKERASAN, DIAMETRALTENSILE STRENGTH DAN WATER SORPTION
(KAJIAN TERHADAP BAHAN RESIN KOMPOSIT 3D PRINTING)
DOI:
https://doi.org/10.34011/jmp2k.v35i1.2613Keywords:
surface hardness, post-curing, resin composite, tensile strength, water sorption, 3D printingAbstract
Teeth that have undergone endodontic treatment often lose significant structure, requiring strong and durable restorations to prevent clinical failure and support long-term function. This study aimed to evaluate the effect of post-curing time on the hardness, diametral tensile strength (DTS), and water sorption of 3D-printed resin composites. An experimental study was conducted using 80 disc-shaped resin composite specimens divided into four groups based on post-curing time duration (5 minutes, 10 minutes, no curing, and control). Hardness was measured using the Vickers Hardness test, DTS with a Universal Testing Machine, and water sorption through immersion in artificial saliva. Hypothesis testing was performed using ANOVA and Post Hoc Tamhane tests. The results showed that increasing the post-curing time significantly improved hardness but did not affect DTS and water sorption. The group with 10 minutes of post-curing time achieved the best results in hardness improvement. The findings indicate that post-curing time positively influences the mechanical and physical properties of resin composites, particularly the hardness of 3D-printed materials. This process enables better polymer densification, resulting in stronger materials resistant to degradation in the oral environment. The duration of post-curing time significantly contributes to optimizing the mechanical and physical properties of 3D-printed resin composites, making it an essential step in manufacturing restorations for the long-term success of dental restorations.
References
F. Mannocci and J. Cowie, “Restoration of endodontically treated teeth,” Br Dent J, vol. 216, no. 6, pp. 341–346, Mar. 2014, doi: 10.1038/sj.bdj.2014.198.
N. D. Ruse and M. J. Sadoun, “Resin-composite blocks for dental CAD/CAM applications,” Dec. 25, 2014, SAGE Publications Inc. doi: 10.1177/0022034514553976.
J. Schweiger, D. Edelhoff, and J. F. Güth, “3d printing in digital prosthetic dentistry: An overview of recent developments in additive manufacturing,”, J Clin Med, vol. 10, no 9, pp. 2010, May 01, 2021, doi: 10.3390/jcm10092010.
S. J. Alzahrani, M. S. Hajjaj, A. A. Azhari, W. M. Ahmed, H. E. Yeslam, and R. M. Carvalho, “Mechanical Properties of Three-Dimensional Printed Provisional Resin Materials for Crown and Fixed Dental Prosthesis: A Systematic Review,” Bioengineering, vol. 10, no. 6, pp. 1-14, Jun. 01, 2023, MDPI. doi: 10.3390/bioengineering10060663.
P. J. Atria et al., “3D-printed resins for provisional dental restorations: Comparison of mechanical and biological properties,” Journal of Esthetic and Restorative Dentistry, vol. 34, no. 5, pp. 804–815, Jul. 2022, doi: 10.1111/jerd.12888.
E. Sonkaya, Z. Gonca, and B. Kürklü, “The Effect of Different Surface Treatments on the Repair of 3D Permanent Resin Restorations by Composite Resin Different surface treatments and repair of 3D permanent resin, PREPRINT (Version 1), vol. 216, no. 6, pp. 341–346, 2022, doi: 10.21203/rs.3.rs-1808447/v1.
R. Daher, S. Ardu, E. di Bella, I. Krejci, and O. Duc, “Efficiency of 3D printed composite resin restorations compared with subtractive materials: Evaluation of fatigue behavior, cost, and time of production,” Journal of Prosthetic Dentistry, vol. 131, no. 5, pp. 943–950, May 2024, doi: 10.1016/j.prosdent.2022.08.001.
A. S. Al-Qahtani et al., “Surface properties of polymer resins fabricated with subtractive and additive manufacturing techniques,” Polymers (Basel), vol. 13, no. 23, Dec. 2021, doi: 10.3390/polym13234077.
Y. A. Al-Dulaijan et al., “Comparative Evaluation of Surface Roughness and Hardness of 3D Printed Resins,” Materials, vol. 15, no. 19, Oct. 2022, doi: 10.3390/ma15196822.
D. S. M. Casselli, C. C. Worschech, L. A. M. S. Paulillo, and C. T. dos S. Dias, “Diametral tensile strength of composite resins submitted to different activation techniques,” Braz Oral Res, vol. 20, no. 3, pp. 214–218, 2006, doi: 10.1590/s1806-83242006000300006.
R. Brożek, K. Pałka, R. Koczorowski, and B. Dorocka-Bobkowska, “Effect of artificial saliva on the mechanical properties of a polymer material reinforced with fiber, used in esthetic tooth restorations,” Dent Med Probl, vol. 57, no. 3, pp. 261–267, Jul. 2020, doi: 10.17219/dmp/118642.
D. Kim et al., “Effects of post-curing time on the mechanical and color properties of three-dimensional printed crown and bridge materials,” Polymers (Basel), vol. 12, no. 11, pp. 1–20, Nov. 2020, doi: 10.3390/polym12112762.
E. Prause et al., “Mechanical properties of 3D-printed and milled composite resins for definitive restorations: An in vitro comparison of initial strength and fatigue behavior,” Journal of Esthetic and Restorative Dentistry, vol. 36, no. 2, pp. 391–401, Feb. 2024, doi: 10.1111/jerd.13132.
I. Hubbezoǧlu, G. Bolayir, O. M. Doǧan, A. Doǧan, A. Özer, and B. Bek, “Microhardness evaluation of resin composites polymerized by three different light sources,” Dent Mater J, vol. 26, no. 6, pp. 845–853, 2007, doi: 10.4012/dmj.26.845.
C. K. Scotti, M. M. de A. C. Velo, F. A. P. Rizzante, T. R. de L. Nascimento, R. F. L. Mondelli, and J. F. S. Bombonatti, “Physical and surface properties of a 3D-printed composite resin for a digital workflow,” Journal of Prosthetic Dentistry, vol. 124, no. 5, pp. 614.e1-614.e5, Nov. 2020, doi: 10.1016/j.prosdent.2020.03.029.
S. Cangül, Ö. Adigüzel, S. Tekin, F. Öztekin, and Ö. Satici, “A comparison of the water absorption and water solubility values of four different composite resin materials,” Cumhuriyet Dental Journal, vol. 21, no. 4, pp. 335–342, 2018, doi: 10.7126/cumudj.449340.
I. Erlita, Y. M. Hernandi, and M. Y. I. Nahzi, “Effect Of Diametral Tensile Strength Of Bulk Fill Composite Resin With The Addition Of Sugarcane Waste Fiber.”, Dentino Jurnal Kedokteran Gigi, vol. 3, no. 1, pp. 43-46, 2018, doi: 10.20527/dentino.v3i1.4599.g4004
S. J. Alzahrani, M. S. Hajjaj, A. A. Azhari, W. M. Ahmed, H. E. Yeslam, and R. M. Carvalho, “Mechanical Properties of Three-Dimensional Printed Provisional Resin Materials for Crown and Fixed Dental Prosthesis: A Systematic Review,” Jun. 01, 2023, MDPI. doi: 10.3390/bioengineering10060663.
V. Truxova, J. Safka, M. Seidl, I. Kovalenko, L. Volesky, and M. Ackermann, “Ceramic 3d printing: Comparison of SLA and DLP technologies,” MM Science Journal, vol. 2020, no. June, pp. 3905–3911, Jun. 2020, doi: 10.17973/MMSJ.2020_06_2020006.
F. Rezaie et al., “3D Printing of Dental Prostheses: Current and Emerging Applications,” Feb. 01, 2023, MDPI. doi: 10.3390/jcs7020080.
J. E. Ryu, Y. L. Kim, H. J. Kong, H. S. Chang, and J. H. Jung, “Marginal and internal fit of 3D printed provisional crowns according to build directions,” Journal of Advanced Prosthodontics, vol. 12, no. 4, pp. 225–232, Aug. 2020, doi: 10.4047/jap.2020.12.4.225.
A. E. Hadi et al., “Effect of Water Absorption Behaviour on Tensile Properties of Hybrid Jute-Roselle Woven Fibre Reinforced Polyester Composites,” International Journal of Automotive and Mechanical Engineering, vol. 18, no. 4, pp. 9170–9178, 2021, doi: 10.15282/IJAME.18.4.2021.02.0705.
S. Sanjeevi et al., “Effects of water absorption on the mechanical properties of hybrid natural fibre/phenol formaldehyde composites,” Sci Rep, vol. 11, no. 1, Dec. 2021, doi: 10.1038/s41598-021-92457-9.